Effect of a minute substitution on the structure and microwave dielectric properties of novel LiCoVO4 ceramics for ULTCC applications

Cheng Liang Huang, Pei En Chiang, Tsung Hsien Hsu

研究成果: Article同行評審

8 引文 斯高帕斯(Scopus)

摘要

The feasibility of novel LiCo1-xAxVO4 (A = Mg, Zn; x = 0–0.09) microwave dielectrics for ULTCC (ultra-low temperature co-fired ceramics) applications was investigated. Continuous solid solutions were formed as expected in the whole composition range and can be indexed in the cubic system with the Fd3m space group. The Raman spectrum of the specimen was also analyzed. All samples can be sintered into dense ceramics (relative density> 97%) at the temperature 650°C. The variation of structure parameters resulted from minutely substituting Co with Mg or Zn has significant effect on the microwave dielectric properties of the specimen. The relative density and dielectric polarizability have significant impact on the ɛr of the specimens. Q × f value is dominated by the density and packing fraction of the ceramics. The τf, however, was mainly controlled by the bond-valence of the samples under a minute substitution. Specimen with 0.01 mol% Zn-substitution at 650°C revealed the highest Q × f of 53,000 GHz along with an εr of 13.2 and a τf of–57.5 ppm/°C. It also exhibited a good Al-cofiring chemical compatibility.

原文English
期刊Journal of Asian Ceramic Societies
DOIs
出版狀態Accepted/In press - 2021

All Science Journal Classification (ASJC) codes

  • 陶瓷和複合材料

指紋

深入研究「Effect of a minute substitution on the structure and microwave dielectric properties of novel LiCoVO4 ceramics for ULTCC applications」主題。共同形成了獨特的指紋。

引用此