Effect of CdO Addition on the Properties of Bi-Contained Superconducting Thick Films Prepared from Rapidly Quenched Amorphous Materials

Masahiro Yoshimura, Tae Hyun Sung, Shigeru Arima, Yutaka Ohya, Sakae Tsutai, Nobuo Ishizawa, Hideomi Koinuma, Zenbe e. Nakagawa

研究成果: Article同行評審

摘要

Substitution of Cd for Ca in Bi2Sr2Ca2Cu3Oy has been studied by using rapid quenching after rapid melting technique. Amorphous materials containing a small amount of CaO phase were obtained as films with about 20 μm thickness. Annealing of the films for Bi2Sr2Ca2-xCdxOy at 870°C for 5 hr in air yielded a superconducting phase with co= 3.0 nm in the composition of x≦0.5. Tc(endpoint) increased and tailing of transition disappeared with increasing Cd contents. A maximum Tc(endpoint) value of 87 K was obtained at the composition of x=0.4. Further substitution of Cd for Ca brought about lowering in Tc, because a semiconducting phase with co = 2.5 nm was formed instead of co = 3.0 nm phase.

原文English
頁(從 - 到)974-978
頁數5
期刊journal of the japan society of powder and powder metallurgy
35
發行號9
DOIs
出版狀態Published - 1988

All Science Journal Classification (ASJC) codes

  • 機械工業
  • 工業與製造工程
  • 金屬和合金
  • 材料化學

指紋

深入研究「Effect of CdO Addition on the Properties of Bi-Contained Superconducting Thick Films Prepared from Rapidly Quenched Amorphous Materials」主題。共同形成了獨特的指紋。

引用此