Effect of grain size and basal texture on tensile properties and fracture characteristics of extruded AZ31 alloy

Hsiang Ching Chen, Truan Sheng Lui, Li Hui Chen

研究成果: Conference contribution

摘要

With different tilting angles corresponding to the basal planes of the extruded Mg-3%Al-1%Zn alloy (0°, 30°, 45°. 60°, 90°), uniaxial tensile tests of the extruded alloy were conducted at room temperature to discuss the effects of basal texture and grain size on its tensile properties and fracture characteristics. Compared to the coarse-grained sample, the fine-grained sample showed obvious increase in the yield stress since the tilting angles were 0° and 90°. However, the total elongation of the fine-grained sample was higher than that of the coarse-grained specimen since the tilting angles ranged from 30° to 60°. According to the observation of fracture surface, a dimple feature was observed in the fine-grained samples. In the contrast, a plate-like feature was recognized on the fracture surface of the sample with coarse grains.

原文English
主出版物標題Magnesium Technology 2013 - Held During the TMS 2013 Annual Meeting and Exhibition
發行者Minerals, Metals and Materials Society
頁面83-87
頁數5
ISBN(列印)9781118605523
DOIs
出版狀態Published - 2013
事件Magnesium Technology 2013 - TMS 2013 Annual Meeting and Exhibition - San Antonio, TX, United States
持續時間: 2013 三月 32013 三月 7

出版系列

名字Magnesium Technology
ISSN(列印)1545-4150

Other

OtherMagnesium Technology 2013 - TMS 2013 Annual Meeting and Exhibition
國家/地區United States
城市San Antonio, TX
期間13-03-0313-03-07

All Science Journal Classification (ASJC) codes

  • 工程 (全部)

指紋

深入研究「Effect of grain size and basal texture on tensile properties and fracture characteristics of extruded AZ31 alloy」主題。共同形成了獨特的指紋。

引用此