Effect of heat treatment on the precipitation and pitting corrosion behavior of 347 SS weld overlay

I. Hsuang Lo, Wen Ta Tsai

研究成果: Article同行評審

44 引文 斯高帕斯(Scopus)

摘要

The effect of heat treatment on the microstructure and corrosion performance of 347 SS weld overlay has been investigated. The microstructure and phase change of the as-welded and post weld heat treated (PWHT) overlays were examined using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Energy dispersive spectroscopy (EDS) was also used for intermetallic phase identification. The results showed that delta-ferrite (δ ferrite) transformed to sigma (σ) phase in the as-welded overlay after a PWHT at 690 °C for 8 h. Pitting corrosion resistance of the weld with or without PWHT was evaluated by conducting potentiodynamic polarization tests in 3.5% NaCl solution. The results showed that the presence of intermetallic σ phase exerted an adverse effect on the pitting corrosion resistance of 347 SS weld overlay.

原文English
頁(從 - 到)137-143
頁數7
期刊Materials Science and Engineering A
355
發行號1-2
DOIs
出版狀態Published - 2003 八月 25

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

指紋 深入研究「Effect of heat treatment on the precipitation and pitting corrosion behavior of 347 SS weld overlay」主題。共同形成了獨特的指紋。

引用此