Effect of nitrogen doping on the electron field emission properties of chemical vapor deposited diamond films

Chuan-Feng Shih, Kuo Shung Liu, I. Nan Lin

研究成果: Conference article同行評審

29 引文 斯高帕斯(Scopus)

摘要

Nitrogen-doped diamond films were successfully synthesized using a urea/methanol saturated solution as a nitrogen source. Scanning electron microscopy (SEM) and Raman spectroscopy revealed that the morphology and quality of the diamond films were not altered due to nitrogen doping. However, increasing the urea/methanol ratio in gas mixture markedly influences the field emission properties of diamond films, which were optimized when the films were grown using H2/CH4/urea = 300:18:6 sccm. The electron field emission of the films can be turned on at a low field as 5.0 V μm-1 and the emission current density as large as Jc = 1019 μA cm-2 can be attained at 21.6 V μm-1 applied field. The effective work function is φe = 0.034 eV.

原文English
頁(從 - 到)1591-1599
頁數9
期刊Diamond and Related Materials
9
發行號9
DOIs
出版狀態Published - 2000 一月 1
事件5th International Conference on Advanced Materials - Beijing, China
持續時間: 1999 六月 131999 六月 18

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Chemistry(all)
  • Mechanical Engineering
  • Physics and Astronomy(all)
  • Materials Chemistry
  • Electrical and Electronic Engineering

指紋 深入研究「Effect of nitrogen doping on the electron field emission properties of chemical vapor deposited diamond films」主題。共同形成了獨特的指紋。

引用此