Effect of pre-calcination of Bi2O3 and Sb2O3 on the densification and varistor properties of low-temperature sintered ZnO-Bi2O3 ceramics

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

This study utilized a conventional solid-state reaction method to sinter Bi2O3-Sb2O3-Co3O4-Mn3O4-Nb2O5 zinc oxide varistors at low temperatures of 860–880 °C. The pyrochlore phase occurs at temperatures ranging from 700 to 900 °C, influencing densification kinetics. The liquid-phase former, Bi2O3, is consumed and reacts to form the pyrochlore secondary phase Zn2Bi3Sb3O14, which inhibits the densification at low temperatures. Bi2O3 and Sb2O3 were pre-calcined at 550 °C to reduce secondary phase Zn2Bi3Sb3O14 formation and Bi2O3 consumption in this study. It was observed that pre-calcination of Bi2O3 and Sb2O3 at 550 °C successfully reduced the formation of the secondary phase Zn2Bi3Sb3O14, lowered the densification temperature of the ZnO-Bi2O3 varistor and improved its performance.

原文English
文章編號1750
期刊Journal of Materials Science: Materials in Electronics
34
發行號25
DOIs
出版狀態Published - 2023 9月

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 原子與分子物理與光學
  • 凝聚態物理學
  • 電氣與電子工程

指紋

深入研究「Effect of pre-calcination of Bi2O3 and Sb2O3 on the densification and varistor properties of low-temperature sintered ZnO-Bi2O3 ceramics」主題。共同形成了獨特的指紋。

引用此