Effect of SiO2 on immobilization of metals and encapsulation of a glass network in slag

Yi Ming Kuo, Ta Chang Lin, Perng Jy Tsai

研究成果: Article同行評審

17 引文 斯高帕斯(Scopus)

摘要

The final disposal of ash from an incinerator is of special concern because of the possibility of its releasing toxic substances. Melting/vitrification has been regarded as a prospective technology of ash treatment. The object of this investigation was to evaluate the effect of silica (SiO2) addition on the immobilization of hazardous metals and the encapsulation of a glass network during the vitrification process. Four specimens with SiO2/fly ash mixing ratios of 0, 0.1, 0.2, and 0.3, respectively, were tested. The mobility of metals in slag was then estimated by a sequential extraction procedure. X-ray diffraction analysis indicates that SiO2 leads to the polymerization of silicates. The encapsulation of aluminum, calcium, and magnesium would not be observed unless adequate amount of SiO2 was added. It was also found that SiO2 addition enhances the formation of a compact and interconnected glass network structure and, thus, contributes to the chemical stability of metals in slag. After vitrification, the mobility of cadmium, copper, iron, chromium, nickel, lead, and zinc was significantly reduced. However, there is no significant correlation between the immobilization of these metals and the addition of SiO2.

原文English
頁(從 - 到)1412-1416
頁數5
期刊Journal of the Air and Waste Management Association
53
發行號11
DOIs
出版狀態Published - 2003 十一月

All Science Journal Classification (ASJC) codes

  • Waste Management and Disposal
  • Management, Monitoring, Policy and Law

指紋 深入研究「Effect of SiO<sub>2</sub> on immobilization of metals and encapsulation of a glass network in slag」主題。共同形成了獨特的指紋。

引用此