Effect of solution and modification treatments on the crack propagation behaviour of Al-7Si alloy under resonant vibration

D. S. Jiang, Truan-Sheng Lui, L. H. Chen

研究成果: Article同行評審

3 引文 斯高帕斯(Scopus)

摘要

In order to investigate the influence of solution treatment and modification treatment on the crack propagation behaviour of Al-7Si alloy under resonant vibration, the unmodified and Sr-modified materials were tested. The experimental results indicate that the resistance to crack propagation is improved after solution treatment for both the unmodified and modified alloys. The improvement of cracking resistance of unmodified alloy is due to the change in the cracking paths from broken-through particles to particle/matrix interfaces. The unmodified alloy possesses better cracking resistance than does the modified alloy after solution treating at 535°C for 2 hours. On the other hand, the modification treatment shows no obvious improvement to cracking resistance. In the modified alloy, the crack paths of the as-cast and solution-treated specimens both preferentially progress toward the interdendritic zones. The as-cast alloy shows this trend more strongly and hence its cracking trajectory is more meandering and branching.

原文English
頁(從 - 到)9-16
頁數8
期刊International Journal of Cast Metals Research
12
發行號1
DOIs
出版狀態Published - 1999 1月 1

All Science Journal Classification (ASJC) codes

  • 材料力學
  • 機械工業
  • 金屬和合金

指紋

深入研究「Effect of solution and modification treatments on the crack propagation behaviour of Al-7Si alloy under resonant vibration」主題。共同形成了獨特的指紋。

引用此