Effects of Bi4Ti3O12 addition on the microstructure and dielectric properties of Mn-doped BaTiO3-based X8R ceramics

T. A. Jain, C. C. Chen, K. Z. Fung

研究成果: Article同行評審

20 引文 斯高帕斯(Scopus)

摘要

The effects of Bi4Ti3O12 on the microstructure and dielectric properties of Mn-doped BaTiO3 were studied using X-ray diffraction (XRD) and transmission electron microscope (TEM). From XRD analysis and scanning electron microscope (SEM) observations, second phase Bi2Ti2O7 was found when the Bi4Ti3O12 content was more than 4 mol%. The grain size was significantly enhanced with increased Bi4Ti3O12 content. The sintering temperature of Mn-doped BaTiO3-based ceramics could be reduced effectively to 1200 °C by doping them with more than 1 mol% Bi4Ti3O12. TEM results show an obvious core-shell structure with 2 mol% Bi4Ti3O12, which was destroyed when the Bi4Ti3O12 content increased from 2 to 4 mol%. It was found that the Curie temperature was shifted to a higher level and the variation of dielectric constant decreased when Bi4Ti3O12 content increased from 0 to 2 mol%. When the Bi4Ti3O12 content was more than 2 mol%, the Curie temperature decreased due to a change of the core-shell structure and secondary phase Bi2Ti2O7. The variation of dielectric constant as compared with that at room temperature was about -25% at -55 °C and less than ±10% at 150 °C. The stable temperature characteristics of the dielectric constant were caused by the presence of the core-shell grain structure. Due to the "clockwise effect", ceramic materials have great potential as EIA X8R-type multilayer ceramic capacitors.

原文English
頁(從 - 到)414-419
頁數6
期刊Journal of Alloys and Compounds
476
發行號1-2
DOIs
出版狀態Published - 2009 5月 12

All Science Journal Classification (ASJC) codes

  • 材料力學
  • 機械工業
  • 金屬和合金
  • 材料化學

指紋

深入研究「Effects of Bi4Ti3O12 addition on the microstructure and dielectric properties of Mn-doped BaTiO3-based X8R ceramics」主題。共同形成了獨特的指紋。

引用此