Effects of fine particle content in al paste on screen printed contact formation and solar cell performance

Hsin Chiao Fang, Chuan Pu Liu, Hung Shuo Chung, Chin Lin Huang

研究成果: Article同行評審

7 引文 斯高帕斯(Scopus)

摘要

Al screen printed Si solar cells are fabricated in a belt system, and the impact of the fine Al particle content in the Al paste on the alloying process in relation to solar cell performance is investigated. Scanning electron microscopy and transmission electron microscopy analyses show that a lack of fine Al particles in the Al paste causes nonuniform back surface field (BSF), Al-rich extrusions at the Al-Si alloy/Si interface with faceting along the {111} planes of Al, and unmelted Si-rich rods in the Al-Si alloy layer after alloying results in lower Voc, Jsc, and fill factor. The quality of the BSF and the Al-Si alloy layer could thus be improved by optimizing the fine Al particle content in the Al paste. Of the four pastes with different fine Al particle contents prepared for comparison, the content of 27 wt % renders the best contact quality, whereas an even higher content would cause a finer-grained polycrystalline Al-Si alloy to form and the fired Al layer to peel off from the Al-Si alloy layer.

原文English
頁(從 - 到)H455-H458
期刊Journal of the Electrochemical Society
157
發行號4
DOIs
出版狀態Published - 2010 三月 26

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 可再生能源、永續發展與環境
  • 表面、塗料和薄膜
  • 電化學
  • 材料化學

指紋

深入研究「Effects of fine particle content in al paste on screen printed contact formation and solar cell performance」主題。共同形成了獨特的指紋。

引用此