Effects of Sr2+ substitution on photoluminescence characteristics of Ba1-x-ySryZrSi3O9:xEu2+ phosphors

Chung Hao Chiang, Syuan Jhih Gong, Han Yu Lin, Ting Shi Zhan, Sheng-Yuan Chu

研究成果: Article

7 引文 斯高帕斯(Scopus)

摘要

In this work, single-phase Ba1-x-ySryZrSi3O9:xEu2+ phosphors were synthesized via the solid-state reaction method. The crystal structure and luminescence properties were investigated using X-ray diffraction and photoluminescence measurements, respectively. An increase of the dopant Sr2+ increased the emission intensity of the phosphors. The peak intensity of the samples was at y = 0.4 under near-ultraviolet light excitation (397 nm). The wavelength of the emission peaks red-shifts slightly from 477 to 483 nm due to the splitting of the 5d energy level. Sr2+ ions have a smaller ionic radius than that of Ba2+ ions, and thus the dopant changes the crystal structure, improving the energy transfer efficiency between luminescence centers. More Eu2+ solid solubility was found in Ba0.6-xSr0.4ZrSi3O9:xEu2+ phosphors (10 mol. %) than in the host BaZrSi3O9 (6 mol. %), which enhanced the emission intensity. In addition, the thermal reliability of the phosphors was studied.

原文English
文章編號223507
期刊Journal of Applied Physics
116
發行號22
DOIs
出版狀態Published - 2014 十二月 14

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

指紋 深入研究「Effects of Sr<sup>2+</sup> substitution on photoluminescence characteristics of Ba<sub>1-x-y</sub>Sr<sub>y</sub>ZrSi<sub>3</sub>O<sub>9</sub>:xEu<sup>2</sup><sup>+</sup> phosphors」主題。共同形成了獨特的指紋。

  • 引用此