Effects of substrate temperature on the film characteristics and gas-sensing properties of copper phthalocyanine films

Yuh Lang Lee, Wen Ching Tsai, Jer Ru Maa

研究成果: Article

73 引文 斯高帕斯(Scopus)

摘要

Copper phthalocyanine thin films were prepared by vacuum deposition at various substrate temperatures onto glass and gold. The effects of substrate temperature and material on film morphology and crystalline structure were studied, and the film characteristics were related to their gas-sensing properties for NO2. We find that CuPc films have fine-grain morphology and small degree of crystallization at low substrate temperature (Td = 28 °C). When Td is elevated to 100 °C, fiber-like morphology was observed on both substrates, with orientation mainly parallel to the substrate. At 150-200 °C, the fibers grow larger without significant change of orientation on glass, but whisker structures with less order were formed on gold. The fiber-like structure prepared at 100 °C has the highest electrical conductivity, which also implies that the stacking axis of the Pc macrocycle is the high conductivity direction. This characteristic also leads to quick response and higher sensitivity of this film to NO2. The effects of substrate temperature on the film characteristics and gas-sensing properties are compared to the heat-annealing effects observed in our previous work.

原文English
頁(從 - 到)352-361
頁數10
期刊Applied Surface Science
173
發行號3-4
DOIs
出版狀態Published - 2001 三月 29

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Condensed Matter Physics
  • Physics and Astronomy(all)
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

指紋 深入研究「Effects of substrate temperature on the film characteristics and gas-sensing properties of copper phthalocyanine films」主題。共同形成了獨特的指紋。

  • 引用此