Effects of substrate temperature on the properties of heavily Al-doped ZnO films by simultaneous r.f. and d.c. magnetron sputtering

Su Shia Lin, Jow Lay Huang, P. Šajgalik

研究成果: Article同行評審

97 引文 斯高帕斯(Scopus)

摘要

Transparent conducting ZnO films were heavily doped with Al (ZnO/Al) by simultaneous r.f. magnetron sputtering of ZnO and d.c. magnetron sputtering of Al. TEM image showed the coexistence of an amorphous Al complex and polycrystalline ZnO. A strong (002) preferential orientation in the ZnO/Al film was caused by the presence of ZnO. According to XRD and XPS analysis, most Al atoms were not in the ZnO crystalline and most oxygen atoms were attributed to the formation of Na zeolite structure. The Na zeolite could result in the neutral impurity scattering and cause low mobility. Electrical conductivity was primarily due to the contribution of Zn, Al interstitial atoms and oxygen vacancies. Little contribution was due to Al donors (AlZn). The resistivity decreased rapidly with the increase of substrate temperature to a minimum of 6.12×10-2 Ω cm at 150 °C, and then slightly increased. The conductivity of films was closely related to the crystallinity, which was dependent on the substrate temperature. The excellent transmission in the visible region decreased substantially at short wavelength near the ultraviolet range for films prepared at various substrate temperatures.

原文English
頁(從 - 到)39-47
頁數9
期刊Surface and Coatings Technology
190
發行號1
DOIs
出版狀態Published - 2005 一月 3

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 凝聚態物理學
  • 表面和介面
  • 表面、塗料和薄膜
  • 材料化學

指紋

深入研究「Effects of substrate temperature on the properties of heavily Al-doped ZnO films by simultaneous r.f. and d.c. magnetron sputtering」主題。共同形成了獨特的指紋。

引用此