Effects of sulfurization and Cu/In ratio on the performance of the CuInS2 solar cell

Chia Hung Tsai, Dillip Kumar Mishra, Chia Ying Su, Jyh Ming Ting

研究成果: Article同行評審

10 引文 斯高帕斯(Scopus)

摘要

SUMMARY: Photovoltaic CuInS2 (CIS) thin films were prepared from thermally evaporated Cu/In precursors, having various Cu/In ratios, under different sulfurization conditions. The sulfurization was carried out in a quartz tube furnace under a steady or flowing H2S/Ar gas mixture at various temperatures ranging from 450 to 550°C. The effects of the Cu/In ratio and sulfurization condition on the grain size, surface morphology, surface roughness, microstructure and defect formation of the resulting CIS films were examined. It was found that the effects depend on the processing conditions. Particularly, we show that sub-bandgap generated defects can be inferred by photoluminescence data. Selected CIS thin films were used as absorber layers for the fabrication of thin film solar cells. The best solar cell efficiency of 6.29% was obtained from the 500°C-sulfurized absorber layer having a Cu/In ratio of 1.8. Effect of absorber layer characteristics on the cell efficiency was also discussed.

原文English
頁(從 - 到)418-428
頁數11
期刊International Journal of Energy Research
38
發行號4
DOIs
出版狀態Published - 2014 三月 25

All Science Journal Classification (ASJC) codes

  • Renewable Energy, Sustainability and the Environment
  • Nuclear Energy and Engineering
  • Fuel Technology
  • Energy Engineering and Power Technology

指紋 深入研究「Effects of sulfurization and Cu/In ratio on the performance of the CuInS<sub>2</sub> solar cell」主題。共同形成了獨特的指紋。

引用此