Electrical properties of single and multiple poly(3,4-ethylenedioxythiophene) nanowires for sensing nitric oxide gas

Hui Hsin Lu, Chia Yu Lin, Tzu Chien Hsiao, Yueh Yuan Fang, Kuo Chuan Ho, Dongfang Yang, Chih Kung Lee, Su Ming Hsu, Chii Wann Lin

研究成果: Article

24 引文 斯高帕斯(Scopus)

摘要

The electrical properties of conducting polymer, poly(3,4-ethylenedioxythiophene) (PEDOT), nanowires were studied to develop nitric oxide (NO) gas sensors with low working temperatures. A nanowire with a diameter of 300 nm was fabricated using dip-pen nanolithography (DPN) across a 55 μm gap between a pair of electrodes. The electrical properties of single or multiple PEDOT nanowires were examined by plotting the current-voltage (I-V) curves in the range -3 V to +3 V at temperatures between 298 K and 393 K. The conductance of parallel wires was normalized with respect to the dimensions of the fabricated nanowires. The single nanowire exhibited nonlinear conductance associated with hysteresis but multiple wires did not. The currents increased with the temperature and the I-V characteristics were consistent with the power law G(T)αTα with α∼ 5.14 and 5.43. The responses to NO were highly linear and reproducible, indicating that sensing using PEDOT nanowires was reliable with a minimal concentration of NO of 10 ppm.

原文English
頁(從 - 到)68-74
頁數7
期刊Analytica Chimica Acta
640
發行號1-2
DOIs
出版狀態Published - 2009 四月 27

All Science Journal Classification (ASJC) codes

  • Analytical Chemistry
  • Biochemistry
  • Environmental Chemistry
  • Spectroscopy

指紋 深入研究「Electrical properties of single and multiple poly(3,4-ethylenedioxythiophene) nanowires for sensing nitric oxide gas」主題。共同形成了獨特的指紋。

  • 引用此