Electrochemical copolymerization of aniline and para-phenylenediamine on IrO2-coated titanium electrode

C. H. Yang, T. C. Wen

研究成果: Article同行評審

98 引文 斯高帕斯(Scopus)

摘要

Copolymerization of aniline (AN) and para-phenylenediamine (PPDA) was electrochemically performed by cyclic voltammetry on IrO2-coated titanium electrodes in 0.5 m H2SO4. The cyclic voltammograms, with and without a middle peak at about 580 mV, can be produced by controlling the PPDA concentration in the aniline solution during polymer preparation. The peak at about 580 mV corresponds to the para-aminophenol/benzoquinoneimine (PAP/QI) redox couple and crosslinking sites. The mass of polymer deposited on an IrO2-coated titanium electrode is correlated with the polymer anodic peak current, which allows the rates of polymer deposition to be monitored by increases in the anodic peak current at various PPDA concentrations. SEM photographs show that the morphology of the polymer film depends dramatically on PPDA concentration. Stability test information can be used in generating an effective index to discern between the crosslinking and the PAP/QI reactions induced by PPDA. The linear relationship between the second redox process potential (E1/2), corresponding to the oxidation and reduction between polaronic emeraldine and pernigraniline in PPDA-modified PANI films, and pH, possesses a slope of about -120 mV/pH.

原文English
頁(從 - 到)166-178
頁數13
期刊Journal of Applied Electrochemistry
24
發行號2
DOIs
出版狀態Published - 1994 二月 1

All Science Journal Classification (ASJC) codes

  • 化學工程 (全部)
  • 電化學
  • 材料化學

指紋

深入研究「Electrochemical copolymerization of aniline and para-phenylenediamine on IrO<sub>2</sub>-coated titanium electrode」主題。共同形成了獨特的指紋。

引用此