Electrochemical corrosion behaviour of Pb-free Sn-8.5Zn-0.05Al-XGa and Sn-3Ag-0.5Cu alloys in chloride containing aqueous solution

Udit Surya Mohanty, Kwang Lung Lin

研究成果: Article同行評審

62 引文 斯高帕斯(Scopus)

摘要

The electrochemical corrosion behaviour of Pb-free Sn-8.5Zn-0.05Al-XGa and Sn-3Ag-0.5Cu alloys was investigated in 3.5% NaCl solution by using potentiodynamic polarization techniques. The results obtained from polarization studies revealed that there was a negative shift in the corrosion potential with increase in Ga content from 0.02 to 0.2 wt% in the Sn-8.5Zn-0.05Al-XGa alloy. These changes were also reflected in the corrosion current density (Icorr) value, corrosion rate and linear polarization resistance (LPR) of the four element alloy. However, for Sn-3Ag-0.5Cu alloy a significant increase in the corrosion rate and corrosion current density was observed as compared to the four element alloys. SIMS depth profile results established that ZnO present on the outer surface of Sn-8.5Zn-0.05Al-0.05Ga alloy played a major role in the formation of the oxide film. Oxides of Sn, Al and Ga contributed a little towards the formation of film on the outer surface of the alloy. On the other hand, Ag2O was primarily responsible for the formation of the oxide film on the outer surface of Sn-3Ag-0.5Cu alloy.

原文English
頁(從 - 到)2437-2443
頁數7
期刊Corrosion Science
50
發行號9
DOIs
出版狀態Published - 2008 九月

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 化學工程 (全部)
  • 材料科學(全部)

指紋

深入研究「Electrochemical corrosion behaviour of Pb-free Sn-8.5Zn-0.05Al-XGa and Sn-3Ag-0.5Cu alloys in chloride containing aqueous solution」主題。共同形成了獨特的指紋。

引用此