Electrochemical polarization and pitting behaviour of Fe-Al-Mn alloys in chloride solutions

Wen Ta Tsai, Jing Bang Duh, Ju Tung Lee

研究成果: Article同行評審

19 引文 斯高帕斯(Scopus)

摘要

The electrochemical polarization behaviour of the austenitic Fe-8.25 Al-29.95 Mn-0.85 C and Fe-9.33 AI-25.94 Mn-1.45 C alloys, either solution-annealed and/or age-treated, was investigated in 3.5 wt% NaCl solution. Potentiodynamic polarization tests showed that these alloys passivated with difficulty and had much higher anodic passive current densities than that of the conventional austenitic 316 stainless steel (SS). The susceptibility to pitting corrosion of these alloys under open-circuit potential conditions was also studied in 6% FeCl3 solution. Metallographical examination indicated that pitting and general corrosion occurred on the specimen surfaces. The corrosion rates of these alloys were about one order of magnitude higher than that of the AlSl 316 SS. In general, the corrosion resistances of the Fe-Al-Mn alloys studied were inferior to that of the conventional stainless steel.[/p]

原文English
頁(從 - 到)3517-3521
頁數5
期刊Journal of Materials Science
22
發行號10
DOIs
出版狀態Published - 1987 十月

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 材料力學
  • 機械工業

指紋

深入研究「Electrochemical polarization and pitting behaviour of Fe-Al-Mn alloys in chloride solutions」主題。共同形成了獨特的指紋。

引用此