Electrochemical properties of LiMn2O4 nano-particles synthesized by citric acid gel process

Yi Ming Hon, Kuan Zong Fung, Shih Pin Lin, Min Hsiung Hon

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

Thermal analysis, phase and electrochemical properties of nano-LiMn2O4 powders synthesized at low temperature by citric acid gel process were investigated. The activation energy for LiMn2O4 formation was 130.8 kJ/mol when lithium manganese citrate was used as a precursor. The lattice parameter and volume of LiMn2O4 powders increased with synthesis temperature increased, which resulted from the decreased average valence of manganese. As the temperature was above 700°C, LiMn2O4 underwent phase transition from a cubic to a tetragonal phase, which was attributed to oxygen removal in the lattice. In cyclic voltammogram (CV) analysis, the two pairs of oxidation and reduction CV curves indicated that, apparently, the insertion and extraction reactions of lithium ion occurred in two stages. The initial discharge capacity of LiMn2O4 powders increased with the increasing calcination temperature, but the powders calcined at lower temperatures exhibited a better cycling behavior than the ones calcined at higher temperatures. The capacity fading of the spinel LiMn2O4 was due to structural damages caused by the Jahn-Teller distortion.

原文English
頁(從 - 到)986-991
頁數6
期刊Journal of the Ceramic Society of Japan
109
發行號1276
DOIs
出版狀態Published - 2001 十二月

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry

指紋 深入研究「Electrochemical properties of LiMn<sub>2</sub>O<sub>4</sub> nano-particles synthesized by citric acid gel process」主題。共同形成了獨特的指紋。

引用此