Electrochemical responses from surface oxides present on HNO3-treated carbons

Pei Zhe Cheng, Hsisheng Teng

研究成果: Article同行評審

80 引文 斯高帕斯(Scopus)

摘要

Carbons of different surface oxide compositions, which were prepared from HNO3 oxidation of polyacrylonitrile-based carbon fabric followed by heat treatment at different temperatures, were subjected to electrochemical response analysis using a voltammetric method. Temperature programmed desorption was employed to analyze the surface oxide composition. A significant amount of unstable oxides that can be irreversibly removed with reduction using a cathodic potential sweep were found to be present on the oxidized carbons. About 2.6 electrons are required to remove one oxygen atom from the carbon surface, and this may be the first quantitative study ever reported. After the initial cathodic sweep, no irreversible reduction peak response was observed for the subsequent electrochemical measurements. The capacitive performance of the carbons is related to the population of stable CO-desorbing complexes that can be determined with thermal desorption after the cathodic sweep. The present work has shown that carbon capacitance increases from 170 to 190 F/g with an increase of the CO-desorbing oxides from 1.31 to 1.56 mmol/g. This means that each stable CO-desorbing oxide is able to store 0.8 electron charge per volt within the potential window employed, suggesting the effective role of CO-desorbing oxides in improving the capacitance.

原文English
頁(從 - 到)2057-2063
頁數7
期刊Carbon
41
發行號11
DOIs
出版狀態Published - 2003

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 材料科學(全部)

指紋

深入研究「Electrochemical responses from surface oxides present on HNO<sub>3</sub>-treated carbons」主題。共同形成了獨特的指紋。

引用此