Electrodeposition of Stoichiometric Indium Antimonide from Room-Temperature Ionic Liquid 1-Butyl-1-Methylpyrrolidinium Dicyanamide

Yi Ting Hsieh, Yu Chen Chen, I. Wen Sun

研究成果: Article同行評審

13 引文 斯高帕斯(Scopus)

摘要

A stoichiometric InSb film was electrodeposited on a nickel (Ni) substrate in a room-temperature ionic liquid, 1-butyl-1-methylpyrrolidinium dicyanamide (BMP-DCA), containing anhydrous InCl3 and SbCl3 with a molar concentration ratio of 1:1. The composition of the deposited InSb film was found to depend on both the applied potential and the deposition charge. Crystalline deposits can be directly obtained at low temperature (60°C) without any post-heat treatment. The optical band gap of the InSb film analyzed by using FTIR spectroscopy measurements was approximately 0.17eV. Results from photocurrent experiments indicate that the electrodeposited InSb film was a p-type semiconductor. IL do it again: Crystallite InSb continuous film was obtained at a low temperature (60°C) from 1-butyl-1-methylpyrrolidinium dicyanamide ionic liquid. Results from photocurrent experiments indicate that the electrodeposited InSb film is a p-type semiconductor.

原文English
頁(從 - 到)638-643
頁數6
期刊ChemElectroChem
3
發行號4
DOIs
出版狀態Published - 2016 四月 1

All Science Journal Classification (ASJC) codes

  • 催化
  • 電化學

指紋

深入研究「Electrodeposition of Stoichiometric Indium Antimonide from Room-Temperature Ionic Liquid 1-Butyl-1-Methylpyrrolidinium Dicyanamide」主題。共同形成了獨特的指紋。

引用此