Electroless nanowelding of silver nanowires at room temperature

Chih Jui Ni, Franklin Chau-Nan Hong

研究成果: Article同行評審

15 引文 斯高帕斯(Scopus)

摘要

Silver nanowires (Ag NWs) using polyvinylpyrrolidone (PVP) surfactants were coated on either polyethylene terephthalate (PET) or glass substrates. The resistance of the Ag NW film was very high due to the PVP molecules wrapping around the Ag NWs and preventing good electrical contacts between them. We performed an Ag electroless deposition (ELD) on the Ag NW film at room temperature and achieved the welding of Ag NWs by enhancing the deposition of Ag right at the junctions of the two crossing wires. The welding of Ag NWs drastically reduced the sheet resistance (Rsh) of the film from 17000 to 20 ohm sq-1for only a 2 min treatment. By conducting the Ag ELD on the PVP-removed Ag NW film annealed at 200 °C, we showed that the PVP molecules concentrated at the junctions were responsible for the nanowelding behavior. In addition, both ethylenediamine (EDA) and ammonium hydroxide (NH4OH) could mildly etch the Ag NWs to remove PVP from the wires at room temperature, improving the contacts between Ag NWs and thus reducing the Rshof the Ag NW film. An organic light emitting diode with ELD-treated Ag NW film was prepared to demonstrate the applicability of the nanowelding technique for conductivity enhancement. The better performance of the device based on ELD-treated Ag NW film compared with that on Ag thin film was due to the higher degree of light transmittance and work function of the Ag NWs.

原文English
頁(從 - 到)40330-40338
頁數9
期刊RSC Advances
4
發行號76
DOIs
出版狀態Published - 2014

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 化學工程 (全部)

指紋

深入研究「Electroless nanowelding of silver nanowires at room temperature」主題。共同形成了獨特的指紋。

引用此