Enhanced Stability, Superior Anti-Corrosive, and Tribological Performance of Al2O3 Water-based Nanofluid Lubricants with Tannic Acid and Carboxymethyl Cellulose over SDBS as Surfactant

Dieter Rahmadiawan, Shih Chen Shi

研究成果: Article同行評審

13 引文 斯高帕斯(Scopus)

摘要

In this research work, the stability, tribological, and corrosion properties of a water-based Al2O3 nanofluid (0.5 wt%) formulated with tannin acid (TA) and carboxymethyl cellulose (CMC) as dispersants or surfactants were investigated. For comparative purposes, sodium dodecylbenzene sulfonate (SDBS) was also incorporated. The stability of the nanofluid was assessed through zeta potential measurements and photo-capturing, revealing the effectiveness of TA and CMC in preventing nanoparticle agglomeration. Tribological properties were examined using a pin-on-disk apparatus, highlighting the tribofilm of Al2O3 that enhanced lubricating properties of the nanofluid by the SEM, resulting in reduced friction and wear of the contacting surfaces. Sample with the addition of both TA and CMC exhibited the best tribological performance, with a ~ 20% reduction in the friction coefficient and a 59% improvement in wear rate compared to neat nanofluid without TA and CMC. Additionally, the corrosion resistance of the nanofluids were evaluated via weight loss and electrochemical impedance spectroscopy. The nanofluid sample containing both TA and CMC exhibited the lowest corrosion rate, with 97.6% improvement compared to sample without them. This study provides valuable insights into the potential applications of TA and CMC-based Al2O3 nanofluids as effective and environmentally friendly solutions for coolant or lubrication in cutting processes.

原文English
文章編號9217
期刊Scientific reports
14
發行號1
DOIs
出版狀態Published - 2024 12月

All Science Journal Classification (ASJC) codes

  • 多學科

指紋

深入研究「Enhanced Stability, Superior Anti-Corrosive, and Tribological Performance of Al2O3 Water-based Nanofluid Lubricants with Tannic Acid and Carboxymethyl Cellulose over SDBS as Surfactant」主題。共同形成了獨特的指紋。

引用此