Enhancement of photocatalytic performance of P25-TiO2 nanoparticles by 3D nanoporous anodic alumina at room temperature

Chen Kuei Chung, Ming Wei Liao, En Hao Kuo, Zhou Wei Wang

研究成果: Article

1 引文 斯高帕斯(Scopus)

摘要

The commercial Degussa P25-TiO2 nanoparticles consisting of a mixed phase are a crucial environmental catalyst but encounter the robust coating problem onto the solid support for poor photocatalysis. Here, we have demonstrated a useful green method for greatly improving water-flushing robust coating as well as photocatalysis by over-etched three-dimensional (3D) nanoporous anodic aluminum oxide (AAO) that can be fabricated by large-scale electrochemical-anodic-oxidation processing at room temperature instead of high-temperature sintering for traditional ceramic foams up to 1200°C. Also, no additional high-temperature calcination of 400~900°C was needed. The 3D porous morphology exhibited more TiO2 particles attachment on the rough surface and enlarged pore channels than the 2D. Moreover, the over-etched 3D AAO exhibited the most attachment of TiO2 nanoparticles after water flushing due to high-porosity-and-contact-area 3D morphology which enhances the bonding between the substrate and nanoparticles for robust coating. XRD and SEM were used for analyzing the mixed phase and 2D-3D morphology of the P25-TiO2 nanoparticles on AAO. After immersion in Methylene blue solution and 20 hour of UV illumination, TiO2 nanoparticles on the over-etched 3D AAO with robust coating showed the best decomposition rate compared to other supports including Si wafer, typical 2D and 3D AAO.

原文English
頁(從 - 到)438-447
頁數10
期刊International Journal of Applied Ceramic Technology
15
發行號2
DOIs
出版狀態Published - 2018 三月 1

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Condensed Matter Physics
  • Marketing
  • Materials Chemistry

指紋 深入研究「Enhancement of photocatalytic performance of P25-TiO<sub>2</sub> nanoparticles by 3D nanoporous anodic alumina at room temperature」主題。共同形成了獨特的指紋。

  • 引用此