Enhancing emission of poly(p-phenylenevinylene) by sandwiching an energy transferable layer

Horng Long Cheng, King Fu Lin

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)

摘要

Photoluminescent (PL) and electroluminescent (EL) efficiencies of poly(p-phenylenevinylene) (PPV) film were found to be significantly increased by sandwiching an energy-transferable poly(2-carboxyphenylene-1,4-diyl) (PCPD) layer. Energy transfer from PCPD to PPV in the prepared PPV/PCPD/PPV trilayer film was detected by photoluminescence excitation (PLE) spectroscopy and time-resolved fluorescence decay profiles, and was attributed to the chemical-interlocking between two polymers in the interracial regions. It resulted in a strong increase of the PL intensity, a ∼250-times increase of the maximum external EL quantum efficiency (up to 1.3% photon/electron), and a ∼500-times increase of the maximum light output for the ITO/PPV/PCPD/PPV/A1 device compared to the neat PPV. The significant increase of EL was also attributed to the higher energy bandgap of inserting PCPD layer that trap the holes and electrons in the interfacial regions, facilitating the formation of excitons in situ and energy transfer.

原文English
頁(從 - 到)2270-2274
頁數5
期刊Journal of Materials Chemistry
12
發行號8
DOIs
出版狀態Published - 2002 八月 1

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Materials Chemistry

指紋 深入研究「Enhancing emission of poly(p-phenylenevinylene) by sandwiching an energy transferable layer」主題。共同形成了獨特的指紋。