Epitaxially grown Fe/Ag ultrathin films on GaAs and their application to wideband microwave notch filter

W. Wu, C. C. Lee, C. S. Tsai, J. Su, W. So, H. J. Yoo, R. Chuang, H. J. Hopster

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

Ultrathin ferromagnetic iron/silver films were epitaxially grown on GaAs substrates by molecule beam epitaxy. Sample magnetization and magnetic anisotropy were studied by magneto-optic Kerr effect experiment. The common features in the ferromagnetic resonance peak-to-peak linewidth ΔHpp are identified, with the narrowest linewidth of 23 Oe. Electronically tunable wideband notch filters utilizing the flip-chip devices have been realized using Fe/Ag film-GaAs waveguide layer structures. The peak absorption carrier frequency of a propagating microwave has been tuned in a range from 9.6 to 21 GHz in a modest magnetic field from 0 to 1650 Oe for single layer structure. For multilayer structures, peak absorption is intensified with tuned range from 10.7 to 27 GHz. The experimental results are in good agreement with the theoretical predictions for the case in which the magnetic field is applied along the easy axis of the Fe film.

原文English
頁(從 - 到)534-539
頁數6
期刊Journal of Crystal Growth
225
發行號2-4
DOIs
出版狀態Published - 2001 五月 1

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Inorganic Chemistry
  • Materials Chemistry

指紋 深入研究「Epitaxially grown Fe/Ag ultrathin films on GaAs and their application to wideband microwave notch filter」主題。共同形成了獨特的指紋。

引用此