Fabrication and characterization of Na0.5K0.5NbO 3-CuNb2O6 lead-free step-down piezoelectric transformers

Ming Ru Yang, Sheng Yuan Chu, I. Hao Chan, Sheng Kai Huang

研究成果: Article同行評審

8 引文 斯高帕斯(Scopus)

摘要

Lead-free (Na0.5K0.5)NbO3 (NKN) ceramics doped with 1 mol CuNb2O6 (01CN) ceramics were prepared using the conventional mixed oxide method at a sintering temperature of 1075°C. NKN 1 mol CuTa2O6 (NKN-01CN) ceramics sintered at 1075°C exhibit excellent hard piezoelectric properties of kp 40, kt 45, and k33 57, with ferroelectric property E c 23 kV/cm. The mechanical quality factor (Qm) is extraordinarily high (1933) and the temperature stability is excellent (Temperature coefficient of frequency (TCF) -154 ppm/°C). The piezoelectric transformer (PT) was fabricated on NKN-01CN lead-free substrates, and the electrical characteristics were investigated. The devices were simplified into an equivalent circuit and analyzed using the MATLAB software package. The simulation results matched the experimental results. By reversing the input and the output, the step-down PT can be easily fabricated using a simple disk-type structure. A maximum efficiency of 93 with a voltage gain of 0.12 was measured, which was in good agreement with the simulation results (a maximum efficiency of 98.7 with a voltage gain of 0.13) for the step-down mode.

原文English
文章編號044503
期刊Journal of Applied Physics
110
發行號4
DOIs
出版狀態Published - 2011 八月 15

All Science Journal Classification (ASJC) codes

  • 物理與天文學 (全部)

指紋

深入研究「Fabrication and characterization of Na<sub>0.5</sub>K<sub>0.5</sub>NbO <sub>3</sub>-CuNb<sub>2</sub>O<sub>6</sub> lead-free step-down piezoelectric transformers」主題。共同形成了獨特的指紋。

引用此