Fabrication and property of titanium dioxide thin film using sol-gel method and CO2 laser annealing

C. K. Chung, S. L. Lin, K. P. Chuang, S. Y. Cheng, K. Y. Shei

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

In this Letter, the sol-gel method and CO2 laser annealing are combined as an effective process for studying phase formation and the hydrophilic property of TiO2 thin film. X-ray diffraction patterns reveal that phase transformation can be controlled by sol-gel solution or laser power. ANSYS software was used to analyse the temperature field during laser treatment processing to confirm the phase transformation temperature of TiO 2 for anatase at 350°C and rutile at 800°C. Contact angle is an index of hydrophilicity of films and related to laser power. As laser power increases from 0.5 to 3.0W, the contact angle of the film decreased from 70° to 45°because of the enhanced hydrophilicity. The photoluminescence (PL) property of the laser annealed films was also studied to find wavelengths of 350-800nm. The wide PL can be deconvoluted into different peaks that were attributed to the lattice emission, deep-level emissions from oxygen vacancies and defect states. This combined processing offers an easy way for the fabrication of hydrophilic and wide PL TiO2 with merits of larger area, selective treatment and low cost.

原文English
頁(從 - 到)701-704
頁數4
期刊Micro and Nano Letters
7
發行號8
DOIs
出版狀態Published - 2012 八月 1

All Science Journal Classification (ASJC) codes

  • Bioengineering
  • Biomedical Engineering
  • Materials Science(all)
  • Condensed Matter Physics

指紋 深入研究「Fabrication and property of titanium dioxide thin film using sol-gel method and CO<sub>2</sub> laser annealing」主題。共同形成了獨特的指紋。

引用此