Fabrication of multilaminated Si3N4-Si3N4/TiN composites and its anisotropic fracture behavior

Jow Lay Huang, Yen Lon Chang, Horng Hwa Lu

研究成果: Article同行評審

17 引文 斯高帕斯(Scopus)

摘要

Laminated composites containing alternate layers of Si3N4 and TiN/Si3N4 materials were used as model material for investigating the crack behaviors and mechanical properties. Results indicated that both strength and toughness in laminated composites were higher than that of monolithic silicon nitride. The failure profiles were affected by the stored strain energy prior to failure and the stress gradient in each layer. Cracks deviated successively from one layer to the other due to periodic stress distribution. Samples with better strength and toughness also had a longer crack propagation path and higher amplitude of crack deviation. The periodic stress distribution in laminated composites was confirmed by the measurements of indentation crack length. Results also suggested a tensile stress in the Si3N4 layer and compressive stress in the TiN/Si3N4 layer, in directions normal to the free sample interface.

原文English
頁(從 - 到)2337-2344
頁數8
期刊Journal of Materials Research
12
發行號9
DOIs
出版狀態Published - 1997 七月 1

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

指紋 深入研究「Fabrication of multilaminated Si<sub>3</sub>N<sub>4</sub>-Si<sub>3</sub>N<sub>4</sub>/TiN composites and its anisotropic fracture behavior」主題。共同形成了獨特的指紋。

引用此