Fabrication of Nonadditive Mica Ceramics by Hot Isostatic Processing

Takeo Hattori; Atsushi Shigemori; Jun‐Ichi ‐I Mohri; Masahiro Yoshimura; Shigeyuki Somiya

doi:10.1111/j.1151-2916.1982.tb10518.x

Fabrication of Nonadditive Mica Ceramics by Hot Isostatic Processing

Takeo Hattori, Atsushi Shigemori, Jun‐Ichi ‐I Mohri, Masahiro Yoshimura, Shigeyuki Somiya

材料科學及工程學系

研究成果: Article › 同行評審

2 引文斯高帕斯（Scopus）

摘要

Powder compacts of synthetic mica (fluorphlogopite) encapsulated in a boro–silicate glass tube were isostatically hot–pressed in a Roy–Tuttle–type pressure vessel. Synthetic mica was sintered to a density of 2.60 g/cm³ (91.2% of theoretical density) without additives under 98 MPa of water at 800°C for 45 min.

原文	English
頁（從 - 到）	c142-c142
期刊	Journal of the American Ceramic Society
卷	65
發行號	9
DOIs	https://doi.org/10.1111/j.1151-2916.1982.tb10518.x
出版狀態	Published - 1982 九月

All Science Journal Classification (ASJC) codes

Ceramics and Composites
Materials Chemistry

存取文件

10.1111/j.1151-2916.1982.tb10518.x

指紋深入研究「Fabrication of Nonadditive Mica Ceramics by Hot Isostatic Processing」主題。共同形成了獨特的指紋。

引用此

@article{9719ce83dcf64ed9aee6d749e4510ff3,

title = "Fabrication of Nonadditive Mica Ceramics by Hot Isostatic Processing",

abstract = "Powder compacts of synthetic mica (fluorphlogopite) encapsulated in a boro–silicate glass tube were isostatically hot–pressed in a Roy–Tuttle–type pressure vessel. Synthetic mica was sintered to a density of 2.60 g/cm3 (91.2% of theoretical density) without additives under 98 MPa of water at 800°C for 45 min.",

author = "Takeo Hattori and Atsushi Shigemori and Mohri, {Jun‐Ichi ‐I} and Masahiro Yoshimura and Shigeyuki Somiya",

year = "1982",

month = sep,

doi = "10.1111/j.1151-2916.1982.tb10518.x",

language = "English",

volume = "65",

pages = "c142--c142",

journal = "Journal of the American Ceramic Society",

issn = "0002-7820",

publisher = "Wiley-Blackwell",

number = "9",

}

TY - JOUR

T1 - Fabrication of Nonadditive Mica Ceramics by Hot Isostatic Processing

AU - Hattori, Takeo

AU - Shigemori, Atsushi

AU - Mohri, Jun‐Ichi ‐I

AU - Yoshimura, Masahiro

AU - Somiya, Shigeyuki

PY - 1982/9

Y1 - 1982/9

N2 - Powder compacts of synthetic mica (fluorphlogopite) encapsulated in a boro–silicate glass tube were isostatically hot–pressed in a Roy–Tuttle–type pressure vessel. Synthetic mica was sintered to a density of 2.60 g/cm3 (91.2% of theoretical density) without additives under 98 MPa of water at 800°C for 45 min.

AB - Powder compacts of synthetic mica (fluorphlogopite) encapsulated in a boro–silicate glass tube were isostatically hot–pressed in a Roy–Tuttle–type pressure vessel. Synthetic mica was sintered to a density of 2.60 g/cm3 (91.2% of theoretical density) without additives under 98 MPa of water at 800°C for 45 min.

UR - http://www.scopus.com/inward/record.url?scp=84987321948&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84987321948&partnerID=8YFLogxK

U2 - 10.1111/j.1151-2916.1982.tb10518.x

DO - 10.1111/j.1151-2916.1982.tb10518.x

M3 - Article

AN - SCOPUS:84987321948

VL - 65

SP - c142-c142

JO - Journal of the American Ceramic Society

JF - Journal of the American Ceramic Society

SN - 0002-7820

IS - 9

ER -