Fabrication of transparent ceramics through melt solidification of near eutectic compositions in HfO2-Al2O3-GdAlO3 system

Shunji Araki, Masahiro Yoshimura

研究成果: Article同行評審

15 引文 斯高帕斯(Scopus)

摘要

Solidification of eutectic melts in multiple oxide systems can produce directionally solidified eutectic composites by slow cooling, while rapid cooling would give the formation of amorphous phases as super cooled liquids. We have successfully fabricated an amorphous bulk ceramics in the ternary system HfO2-Al2O3-GdAlO3 for the first time. It has the near eutectic composition of HfO2 (14 mol%), Al2O3 (63 mol%) and Gd2O3 (23 mol%) and highly transparent, >85%, in the visible region after the cooling of around 200-500 K/s for 2-5 mm Ø globules. The sample had kept amorphous up to 1073 K but crystallized above 1273 K then lost the transparency. The formation of an amorphous phase could be discussed by the equilibrated temperature (T0) lines in meta-stable phase diagram. The present study suggests possible formation of transparent bulk ceramics by the melt-solidification of eutectic melts in various ternary or multiple phase systems.

原文English
頁(從 - 到)3295-3299
頁數5
期刊Journal of the European Ceramic Society
26
發行號15
DOIs
出版狀態Published - 2006

All Science Journal Classification (ASJC) codes

  • 陶瓷和複合材料
  • 材料化學

指紋

深入研究「Fabrication of transparent ceramics through melt solidification of near eutectic compositions in HfO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-GdAlO<sub>3</sub> system」主題。共同形成了獨特的指紋。

引用此