Field-emission characteristics of Al-doped ZnO nanostructures hydrothermally synthesized at low temperature

Po Yu Yang, Jyh Liang Wang, Wei Chih Tsai, Shui-Jinn Wang, Jia Chuan Lin, I. Che Lee, Chia Tsung Chang, Huang Chung Cheng

研究成果: Article

17 引文 斯高帕斯(Scopus)

摘要

The aluminum-doped ZnO (AZO) nanostructures with different Al concentrations were synthesized on AZO/glass substrate via a simple hydrothermal growth method at a temperature as low as 85 °C. The morphologies, crystallinity, optical emission properties, and chemical bonding states of AZO nanostructures show evident dependence on the aluminum dosage. The morphologies of AZO nanostructures were changed from vertically aligned nanowires (NWs), and NWs coexisted with nanosheets (NSs), to complete NSs in respect of the Al-dosages of 0∼3 at.%, 5 at.%, and 7 at.%, correspondingly. The undoped ZnO and lightly Al-doped AZO (≦3 at.%) NWs are single-crystalline wurtzite structure. In contrast, heavily Al-doped AZO sample is polycrystalline. The AZO nanostructure with 3 at.% Al-dosages reveals the optimal crystallinity and less structural defects, reflecting the longest carrier lifetime and highest conductivity. Consequently, the field-emission characteristics of such an AZO emitter can exhibit the higher current density, larger field-enhancement factor (β) of 3131, lower turn-on field of 2.17 V/μm, and lower threshold field of 3.43 V/μm.

原文English
頁(從 - 到)6013-6019
頁數7
期刊Journal of Nanoscience and Nanotechnology
11
發行號7
DOIs
出版狀態Published - 2011 七月 1

All Science Journal Classification (ASJC) codes

  • Bioengineering
  • Chemistry(all)
  • Biomedical Engineering
  • Materials Science(all)
  • Condensed Matter Physics

指紋 深入研究「Field-emission characteristics of Al-doped ZnO nanostructures hydrothermally synthesized at low temperature」主題。共同形成了獨特的指紋。

  • 引用此