Field emission characteristics of amorphous diamond

Ming Chi Kan, Jow Lay Huang, James Sung, Ding Fwu Lii, Kuei Hsien Chen

研究成果: Article

5 引文 斯高帕斯(Scopus)

摘要

Amorphous diamond is diamond-like carbon (DLC) that contains no other impurities. It can be conveniently deposited by bombarding a substrate with a cathodic arc. The arc contains a flux of ionized carbon atoms that are driven by a negative bias. In this research, this bias is set at 20 V. Various forms of amorphous diamond were deposited on silicon substrate of n-type (100) by varying the arc current set at 30, 50, 80, and 100 A. The sp3/(sp3 + sp2) ratios of these deposited coatings were measured by electron spectroscopy for chemical analysis and Raman spectroscopy, and the asperity height these films were imaged by an atomic force microscope. It was found that the sp3/(sp3 + sp2) ratio peaked at a value of about 50% when the current was set at 80 A. The average roughness increased linearly with the increasing current from ∼0.5 nm at 30 A to about 1.1 nm at 100 A. The maximum asperity height was approximately 10 times that of the above average roughness figures in all cases. The minimum effective work function (Φe) calculated by a Fowler-Nordheim plot was about 0.063 14 eV. By controlling the asperity height of amorphous diamond, high-emitting efficiencies could be achieved with good reproducibility.

原文English
頁(從 - 到)1513-1517
頁數5
期刊Journal of the American Ceramic Society
86
發行號9
DOIs
出版狀態Published - 2003 七月 1

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

指紋 深入研究「Field emission characteristics of amorphous diamond」主題。共同形成了獨特的指紋。

  • 引用此