Field emission properties of self-assembled InN nano-structures: Effect of Ga incorporation

C. F. Shih, N. C. Chen, P. H. Chang, K. S. Liu

研究成果: Article

10 引文 斯高帕斯(Scopus)

摘要

This work reports the field emission properties of InN and In-rich InGaN nano-structures. Pyramid InN with a tip-like feature exhibits field emission characteristics in a vacuum. Adding Ga into InN reduces the surface roughness and degrades the turn-on electric field. However, when the Ga content is as low as 2%, the same roughness of the film is almost maintained and the barrier height is lower than that of InN. Ultraviolet photoemission spectroscopic analyses show a gradual reduction on the surface work function of InGaN films when the Ga content increases. From the perspectives of surface roughness and surface work function, the In0.98Ga0.02N sample has the best field emission properties of all of the samples studied herein. A turn-on field of 11 V/μm and an emission current density of 1×10-2 A/cm2 (at 30 V/μm) in the In0.98Ga0.02N epilayer were achieved.

原文English
頁(從 - 到)328-333
頁數6
期刊Journal of Crystal Growth
281
發行號2-4
DOIs
出版狀態Published - 2005 八月 1

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Inorganic Chemistry
  • Materials Chemistry

指紋 深入研究「Field emission properties of self-assembled InN nano-structures: Effect of Ga incorporation」主題。共同形成了獨特的指紋。

  • 引用此