Flexible Heteroepitaxy of CoFe2O4/Muscovite Bimorph with Large Magnetostriction

Heng Jui Liu, Chih Kuo Wang, Dong Su, Tahta Amrillah, Ying Hui Hsieh, Kun Hong Wu, Yi Chun Chen, Jenh Yih Juang, Lukas M. Eng, Shien Uang Jen, Ying Hao Chu

研究成果: Article

41 引文 斯高帕斯(Scopus)

摘要

A bimorph composed of ferrimagnetic cobalt ferrite (CoFe2O4, CFO) and flexible muscovite was fabricated via van der Waals epitaxy. The combination of X-ray diffraction and transmission electron microscopy was conducted to reveal the heteroepitaxy of the CFO/muscovite system. The robust magnetic behaviors against mechanical bending were characterized by hysteresis measurements and magnetic force microscopy, which maintain a saturation magnetization (Ms) of ∼120-150 emu/cm3 under different bending states. The large magnetostrictive response of the CFO film was then determined by digital holographic microscopy, where the difference of magnetostrction coefficient (δ λ) is -104 ppm. The superior performance of this bimorph is attributed to the nature of weak interaction between film and substrate. Such a flexible CFO/muscovite bimorph provides a new platform to develop next-generation flexible magnetic devices.

原文English
頁(從 - 到)7297-7304
頁數8
期刊ACS Applied Materials and Interfaces
9
發行號8
DOIs
出版狀態Published - 2017 三月 1

All Science Journal Classification (ASJC) codes

  • Materials Science(all)

指紋 深入研究「Flexible Heteroepitaxy of CoFe<sub>2</sub>O<sub>4</sub>/Muscovite Bimorph with Large Magnetostriction」主題。共同形成了獨特的指紋。

  • 引用此

    Liu, H. J., Wang, C. K., Su, D., Amrillah, T., Hsieh, Y. H., Wu, K. H., Chen, Y. C., Juang, J. Y., Eng, L. M., Jen, S. U., & Chu, Y. H. (2017). Flexible Heteroepitaxy of CoFe2O4/Muscovite Bimorph with Large Magnetostriction. ACS Applied Materials and Interfaces, 9(8), 7297-7304. https://doi.org/10.1021/acsami.6b16485