Formation and device application of Ge nanowire heterostructures via rapid thermal annealing

Jianshi Tang, Chiu Yen Wang, Faxian Xiu, Yi Zhou, Lih Juann Chen, Kang L. Wang

研究成果: Review article同行評審

21 引文 斯高帕斯(Scopus)

摘要

We reviewed the formation of Ge nanowire heterostructure and its field-effect characteristics by a controlled reaction between a single-crystalline Ge nanowire and Ni contact pads using a facile rapid thermal annealing process. Scanning electron microscopy and transmission electron microscopy demonstrated a wide temperature range of 400∼500C to convert the Ge nanowire to a single-crystalline Ni2Ge/Ge/Ni2Ge nanowire heterostructure with atomically sharp interfaces. More importantly, we studied the effect of oxide confinement during the formation of nickel germanides in a Ge nanowire. In contrast to the formation of Ni 2Ge/Ge/Ni2Ge nanowire heterostructures, a segment of high-quality epitaxial NiGe was formed between Ni2Ge with the confinement of Al2O3 during annealing. A twisted epitaxial growth mode was observed in both two Ge nanowire heterostructures to accommodate the large lattice mismatch in the NixGe/Ge interface. Moreover, we have demonstrated field-effect transistors using the nickel germanide regions as source/drain contacts to the Ge nanowire channel. Our Ge nanowire transistors have shown a high-performance p-type behavior with a high on/off ratio of 105 and a field-effect hole mobility of 210cm2/Vs, which showed a significant improvement compared with that from unreacted Ge nanowire transistors.

原文English
文章編號316513
期刊Advances in Materials Science and Engineering
2011
DOIs
出版狀態Published - 2011

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 工程 (全部)

指紋

深入研究「Formation and device application of Ge nanowire heterostructures via rapid thermal annealing」主題。共同形成了獨特的指紋。

引用此