Grain boundary evolution of cold-rolled FePd alloy during recrystallization at disordering temperature

Hung Pin Lin, Delphic Chen, Jui Chao Kuo

研究成果: Article同行評審

13 引文 斯高帕斯(Scopus)

摘要

In this study, the grain boundary character and texture of 50% and 90% cold-rolled FePd alloy was investigated during recrystallization at 700 °C. Electron backscatter diffraction (EBSD) measurements were performed on the rolling direction to normal direction section. Kernel average misorientation (KAM) calculated from EBSD measurements was employed to determine the recrystallization fraction. The Avrami exponent n of recrystallization is 1.9 and 4.9 for 50% and 90% cold rolling, respectively. The new formation of texture reveals random texture during the recrystallization process. As annealing time increased, the number of high angle boundary (HAGB) and coincidence site lattice (CSL) increased with consumption of low angle boundary (LAGB). In addition, possible transformations between different grain boundaries are observed here.

原文English
頁(從 - 到)3254-3267
頁數14
期刊Materials
8
發行號6
DOIs
出版狀態Published - 2015

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)

指紋

深入研究「Grain boundary evolution of cold-rolled FePd alloy during recrystallization at disordering temperature」主題。共同形成了獨特的指紋。

引用此