Green synthesis of calcium and phosphate compounds by varying ph value and ca/p atomic ratio using aqueous precipitations

Wen Cheng Chen, Chien Ping Ju, Wen Hsien Cheng, Jiin Huey Chernlin

研究成果: Article同行評審

3 引文 斯高帕斯(Scopus)

摘要

Using an aqueous synthesis with varying pH values and changing ion source of calcium-to-phosphorus atomic ratios to clarify precipitations was the purpose of this study. The precipitation procedures were processed in two ways; firstly, a pH range of 3.0 to 12.0 was controlled while the ion source of relative Ca/P ratio was kept at 2.0. Secondly, the reaction was kept alkaline with a pH of 12.0 and the value range of Ca/P ratios in the precursor ion-solutions was 1.0 to 3.0. The physicochemical properties were measured to characterize the various precipitates. Results showed that when the pH was varied, the morphology of the precipitates gradually changed to micrometer column-like shape under acidic condition and nano-scale globular-like shape in alkaline environments. By controlling the pH and Ca/P ratio of ion-sources in aqueous reactions, precipitates in biphasics of calcium carbonate/apatite and calcium hydroxide/apatite were obtained with nanometer-scale morphologies. The precipitation procedures that are used in the synthesis of the biphasics provide a simpler, safer, less expensive and more environmentally friendly than the co-precipitation by sintering processes.

原文English
頁(從 - 到)14-21
頁數8
期刊Ceramics - Silikaty
57
發行號1
出版狀態Published - 2013

All Science Journal Classification (ASJC) codes

  • 分析化學
  • 陶瓷和複合材料
  • 一般化學工程
  • 物理與理論化學
  • 材料化學

指紋

深入研究「Green synthesis of calcium and phosphate compounds by varying ph value and ca/p atomic ratio using aqueous precipitations」主題。共同形成了獨特的指紋。

引用此