Heat-treatment induced material property variations of Al-coated Mg alloy prepared in aluminum chloride/1-ethyl-3-methylimidazolium chloride ionic liquid

Mu Huan Chuang, Jeng Kuei Chang, Pin Ju Tsai, Wen-Ta Tsai, Ming Jay Deng, I-Wen Sun

研究成果: Article同行評審

22 引文 斯高帕斯(Scopus)

摘要

An Al coating film, electrodeposited on a Mg alloy from aluminum chloride-1-ethyl-3-methylimidazolium chloride (AlCl3-EMIC) ionic liquid, effectively prevents the substrate from rapid corrosion in a hostile environment. The thickness of the Al film can be easily determined by controlling the total cathodic charge applied, because the current efficiency of the electrodeposition reaction is close to 100%. Heat treatment at 450°C under an argon atmosphere for 10min causes an inter-diffusion at the Al/Mg interface, optimizing the protective performance of the coating film. Prolonging heating leads to a Mg17Al12 intermetallic phase and a Mg solid solution phase to be formed at the expense of the deposited Al film. This phase transformation gives rise to a degradation in the corrosion resistance of the Al-coated sample.

原文English
頁(從 - 到)200-204
頁數5
期刊Surface and Coatings Technology
205
發行號1
DOIs
出版狀態Published - 2010 九月 1

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 凝聚態物理學
  • 表面和介面
  • 表面、塗料和薄膜
  • 材料化學

指紋

深入研究「Heat-treatment induced material property variations of Al-coated Mg alloy prepared in aluminum chloride/1-ethyl-3-methylimidazolium chloride ionic liquid」主題。共同形成了獨特的指紋。