High Brightness InGaN Green LEDs with an ITO on n++ -SPS Upper Contact

C. S. Chang, Shoou-Jinn Chang, Y. K. Su, C. H. Kuo, Wei-Chi Lai, Yu-Cheng Lin, Y. P. Hsu, S. C. Shei, J. M. Tsai, H. M. Lo, J. C. Ke, Jinn-Kong Sheu

研究成果: Article

28 引文 斯高帕斯(Scopus)

摘要

Indium tin oxide (ITO) (260 nm) and Ni (5 nm)/Au (10 nm) films were deposited onto glass substrates, p-GaN layers, n+ -InGaN/GaN short-period-superlattice (SPS), n++ -SPS and nitride-based green light-emitting diodes (LEDs). It was found that ITO could provide us an extremely high transparency (i.e., 95% at 520 nm). It was also found that the 1.03 × 10-3 ωcm2 specific contact resistance of ITO on n++ -SPS was reasonably small. Although forward voltage of the LED with ITO on n++ -SPS upper contact was slightly higher than that of the LED with Ni/Au on n++ -SPS upper contact, 20 Ma output power and external quantum efficiency of the green LED with ITO on n ++ -SPS upper contact could reach 4.98 m W and 8.2%, respectively, which were much larger than those observed from the green LED with Ni/Au on n++ -SPS upper contact. The reliability of ITO on n++ -SPS upper contact was also found to be reasonably good.

原文English
頁(從 - 到)2208-2212
頁數5
期刊IEEE Transactions on Electron Devices
50
發行號11
DOIs
出版狀態Published - 2003 十一月 1

    指紋

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Electrical and Electronic Engineering

引用此

Chang, C. S., Chang, S-J., Su, Y. K., Kuo, C. H., Lai, W-C., Lin, Y-C., Hsu, Y. P., Shei, S. C., Tsai, J. M., Lo, H. M., Ke, J. C., & Sheu, J-K. (2003). High Brightness InGaN Green LEDs with an ITO on n++ -SPS Upper Contact. IEEE Transactions on Electron Devices, 50(11), 2208-2212. https://doi.org/10.1109/TED.2003.819091