High-frequency noise absorption of Ag-Fe3O4 films on microstrip transmission line

Yu Jen Chou, Lih Shan Chen, Mau Phon Houng

研究成果: Article

2 引文 斯高帕斯(Scopus)

摘要

This paper proposes Ag-Fe3O4 films as a novel noise absorption material for the microstrip transmission line to replace current magnetic materials. The effect of the Ag-Fe3O4 films on a microstrip transmission line for high-frequency noise absorption is discussed. Ag-Fe3O4 films were prepared using the spin-coating technique and deposited on FR4 substrates. The film thickness was approximately 25-75 μm and sheet resistance was controlled in the range of 450-150 Ω. Crystal structures of Ag-Fe3O4 films were conducted using the X-ray diffraction technique. The radio frequency properties of these films were measured using an Agilent Technologies E8364A vector network analyzer in the frequency range of 1-20 GHz. The experimental results show that the composite sheet in the broadband frequency region effectively absorbs the electromagnetic noise, exhibiting a power loss greater than 70% in the frequency range of 6-20 GHz.

原文English
文章編號6847228
期刊IEEE Transactions on Magnetics
51
發行號4
DOIs
出版狀態Published - 2015 四月 1

    指紋

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Electrical and Electronic Engineering

引用此