High-Pressure Resistivity of YFe2Si2 and Magnetic Studies of Y1−yHo yFe2Si2 and YFe2(Si1−xGe x)2 Systems

I. Felner, Bing Lv, K. Zhao, C. W. Chu

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)

摘要

High-pressure resistivity measurements (up to 18.8 kbar) indicate that YFe2Si2 is not superconducting (SC) down to 1.2 K. On the other hand, a clear magnetic peak is observed at 232 K. This peak was recently proposed to a new nearly ferromagnetic Fermi-liquid (NFFL) state. By chemical substitutions of magnetic Ho ions in the nonmagnetic Y site and/or C or Ge in the Si sites of YFe2Si2, we show that this peak is affected and shifted to lower temperatures by three factors: (i) lattice parameters caused by chemical substitution, (ii) applied magnetic field, and (iii) disorder induced by substitution in the Si sites. While Ho substitution does not change much the peak position, both isovalent C and Ge substitutions shift the peak to lower temperature, e.g., in YFe2SiGe the peak position drops to 11 K, indicating that the dominant factor is the disorder induced in the Si site. None of investigated materials is SC down to 1.8 K. Apparently, in all compounds studied, the Fe ions are nonmagnetic, and it is assumed that all magnetic peaks reported here represent this new NFFL state previously proposed for YFe2Si2.

原文English
頁(從 - 到)1207-1216
頁數10
期刊Journal of Superconductivity and Novel Magnetism
28
發行號4
DOIs
出版狀態Published - 2015 四月 1

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 凝聚態物理學

指紋

深入研究「High-Pressure Resistivity of YFe<sub>2</sub>Si<sub>2</sub> and Magnetic Studies of Y<sub>1−y</sub>Ho<sub> y</sub>Fe<sub>2</sub>Si<sub>2</sub> and YFe<sub>2</sub>(Si<sub>1−x</sub>Ge<sub> x</sub>)<sub>2</sub> Systems」主題。共同形成了獨特的指紋。

引用此