High pressure study of the normal and superconducting states of the layered pnictide oxide Ba1-x NaxTi2Sb2O with x = 0, 0.10, and 0.15

M. Gooch, P. Doan, B. Lorenz, Z. J. Tang, A. M. Guloy, C. W. Chu

研究成果: Article同行評審

10 引文 斯高帕斯(Scopus)

摘要

Here we present a systematic study of the effects of pressure on the superconducting and spin/charge density wave (SDW/CDW) transitions of Ba 1-xNaxTi2Sb2O (x = 0, 0.10, and 0.15) by means of resistivity measurements. For x = 0 and 0.10, external pressure results in a decease of the SDW/CDW transition temperature Tc; however, no measurable change is observed for the x = 0.15. The pressure effect on the superconducting transition temperature is different for all three samples. For BaTi2Sb2O (x = 0), Tc increases significantly from 1.2 K at zero pressure to ∼2.9 K at 16.1 kbar. The 10% Na-doped sample shows an initial Tc increase up to 4.2 K with pressure which saturates at higher pressure values. For higher Na concentrations (x = 0.15), Tc continuously decreases with increasing pressure.

原文English
文章編號125011
期刊Superconductor Science and Technology
26
發行號12
DOIs
出版狀態Published - 2013 十二月

All Science Journal Classification (ASJC) codes

  • 陶瓷和複合材料
  • 凝聚態物理學
  • 金屬和合金
  • 電氣與電子工程
  • 材料化學

指紋

深入研究「High pressure study of the normal and superconducting states of the layered pnictide oxide Ba<sub>1-x</sub> Na<sub>x</sub>Ti<sub>2</sub>Sb<sub>2</sub>O with x = 0, 0.10, and 0.15」主題。共同形成了獨特的指紋。

引用此