High-temperature tensile deformation and thermal cracking of ferritic spheroidal graphite cast iron

C. P. Cheng, S. M. Chen, T. S. Lui, L. H. Chen

研究成果: Article

12 引文 斯高帕斯(Scopus)

摘要

Ferritic spheroidal graphite (SG) cast irons of different silicon contents were used to study the tensile 1 behavior in the temperature range of 500 °C to near Ac1. The thermal-cracking behavior under cyclic heating to various temperatures from 650 °C to 850 °C was also explored. According to the tensile data, the temperature dependence of the flow stress is concave upward, and that of the elongation is concave downward with drastic descent after reaching the maximum. The temperature range of ascending stress and descending elongation is above Ac1, in which the eutectic cell-wall region transforms to austenite. Intergranular fracture with serious ductility loss can take place at 500 °C, if the silicon content is too high (3.9 wt pet in this test). This brittle phenomenon can be eliminated through microstructure refining. As to the thermal-cycling test, it indicates that the thermal cracking occurs through intergranular fracture. Whereas the susceptibility to thermal cracking increases with increasing silicon content, it can be reduced by refining the microstructure. Unlike the cast irons heated above Ac1 with phase transformation, the heating temperature of about 750 °C leads to the most severe thermal cracking. In addition, the specimens heated in air have lower thermal-cracking resistance than those heated in a neutral salt bath.

原文English
頁(從 - 到)325-333
頁數9
期刊Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
28
發行號2
DOIs
出版狀態Published - 1997 一月 1

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys

指紋 深入研究「High-temperature tensile deformation and thermal cracking of ferritic spheroidal graphite cast iron」主題。共同形成了獨特的指紋。

  • 引用此