High thermal conductivity ceramics from combustion synthesized AlN powder through microwave sintering and reheating

Shyan-Lung Chung, T. I. Tsai, S. C. Huang

研究成果: Article

1 引文 斯高帕斯(Scopus)

摘要

Combustion synthesized AlN powders were investigated for use as starting material for obtaining high thermal conductivity specimens by microwave sintering and reheating. Microwave sintering and reheating were carried out in a TE 103 single mode cavity with an adjustable microwave power in the range 0-3 kW at 2.45 GHz. Densification was found to be a primary requirement to obtain a high thermal conductivity AlN. AlN powders with good sinterability are required to achieve a high densification. AlN powder with D 50 of ∼6 μm was found to have a poor sinterability that with D 50 of ∼3 μm or finer, a good sinterability. Oxygen content was found to be another important factor determining the thermal conductivity. The thermal conductivity can be enhanced from ∼130 to ∼155 W/m K when the oxygen content is reduced from 2.3 to 1.4 wt %. The thermal conductivity can be significantly improved by microwave reheating of the sintered specimen under a reducing atmosphere. This is considered to be due to enhanced removal of the second phases by the reducing atmosphere.

原文English
頁(從 - 到)45-50
頁數6
期刊International Journal of Self-Propagating High-Temperature Synthesis
21
發行號1
DOIs
出版狀態Published - 2012 三月 1

    指紋

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Process Chemistry and Technology

引用此