Highly conductive PEDOT:PSS film made with ethylene-glycol addition and heated-stir treatment for enhanced photovoltaic performances

Ta Cheng Wei, Shih Hsiu Chen, Chia Yun Chen

研究成果: Article同行評審

15 引文 斯高帕斯(Scopus)

摘要

Highly conductive and stable PEDOT:PSS films were prepared by ethylene-glycol (EG) addition and heated-stir treatment that enhanced the electric conductivity up to 1228.4 S cm-1. Analysis of the long-term figure-of-merit (FoM) performances of EG-treated films with respect to variations in stirring temperatures indicated that the highest value of 78.5 was realized by the facile heated-stir treatment at 90 °C. The underlying mechanism was validated by the synergetic effect of reordering linear PEDOT chains and the effective removal of water via the supplement of thermal energy that considerably displayed the improved film conductivity based on the formation of interconnected PEDOT structures. Furthermore, via combining treated PEDOT:PSS films and Si nanowires, high-performance hybrid solar cells were realized. This was accomplished by reduced charge-transfer resistance and sound heterojunction characteristics that facilitated the charge separation and eventual charge collection by the electrode, thus contributing to the enhancement efficiency. The optimal heated-stir treatment at 90 °C led to improved cell conversion efficiency achieving 12.2%, which was 1.3 times higher than the result based on the conventional room-temperature process.

原文English
頁(從 - 到)3302-3309
頁數8
期刊Materials Chemistry Frontiers
4
發行號11
DOIs
出版狀態Published - 2020 11月

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 材料化學

指紋

深入研究「Highly conductive PEDOT:PSS film made with ethylene-glycol addition and heated-stir treatment for enhanced photovoltaic performances」主題。共同形成了獨特的指紋。

引用此