Highly efficient and stable blue-light-emitting copolyfluorene consisting of carbazole, oxadiazole, and charge-trapping anthracene groups

Ruei Tang Chen, Wen Fen Su, Yun Chen

研究成果: Article同行評審

11 引文 斯高帕斯(Scopus)

摘要

This article presents the synthesis and electroluminescent (EL) properties of a stable blue-light-emitting copolyfluorene (P1) consisting of carbazole, oxadiazole and charge-trapping anthracene groups by Suzuki coupling reaction. The hole-transporting carbazole and electron-transporting oxadiazole improve charges injection and transporting properties, whereas the anthracene is the ultimate emitting chromophore. The thermal, photophysical, electrochemical, and EL properties of P1 were investigated by thermogravimetric analysis, differential scanning calorimeter, optical spectroscopy, cyclic voltammetry, and EL devices fabrication and characterization. P1 demonstrated high-thermal stability with thermal decomposition and glass tranistion temperatures above 400 and 145°C, respectively. In film state, P1 showed blue emission at 451 nm attributed to anthracene chromophore. Photophysical and electrochemical investigations demonstrate that effective energy transfer from fluorene to anthracene segments and charges trapping on anthracene segments leads to efficient and stable blue emission originating from anthracence. Polymer light-emitting diodes using P1 as the emitting layer (ITO/PEDOT:PSS/P1/Ca/Al) exhibited excellent current efficiency (5.1 cd/A) with the CIE coordinate being (0.16, 0.11). The results indicate that copolyfluorene is a promising candidate for the blue-emitting layer in the fabrication of efficient PLEDs.

原文English
頁(從 - 到)184-191
頁數8
期刊Journal of Polymer Science, Part A: Polymer Chemistry
49
發行號1
DOIs
出版狀態Published - 2011 一月 1

All Science Journal Classification (ASJC) codes

  • Polymers and Plastics
  • Organic Chemistry
  • Materials Chemistry

指紋 深入研究「Highly efficient and stable blue-light-emitting copolyfluorene consisting of carbazole, oxadiazole, and charge-trapping anthracene groups」主題。共同形成了獨特的指紋。

引用此