Highly efficient dye-sensitized solar cell with a ZnO nanosheet-based photoanode

Chia Yu Lin, Yi Hsuan Lai, Hsin Wei Chen, Jian Ging Chen, Chung Wei Kung, R. Vittal, Kuo Chuan Ho

研究成果: Article同行評審

208 引文 斯高帕斯(Scopus)


Zinc oxide (ZnO) nanosheets (ZnO-NS) were prepared for the photoanode of a dye-sensitized solar cell (DSSC), first by directly growing layered hydroxide zinc carbonate (LHZC) on an FTO substrate using a chemical bath deposition (CBD) method and then by transforming the LHZC into ZnO through pyrolysis at 300 °C. A light-to-electricity conversion efficiency (η) of 6.06% was achieved for the DSSC with ZnO-NS as its photoanode, under 100 mW cm -2 illumination, and this (η) was found to be much higher than that of the DSSC with ZnO nanoparticles (ZnO-NP) as the photoanode (2.92%). The far superior performance of the DSSC with ZnO-NS is essentially attributed to (i) higher effective electron diffusion coefficient of ZnO-NS (3.59 × 10 -3 cm 2 s -1) than that of ZnO-NP (1.12 × 10 -3 cm 2 s -1), and to (ii) higher dye loading on ZnO-NS (2.66 × 10 -7 mol cm -2) than that on ZnO-NP (1.99 × 10 -7 mol cm -2); this higher electron diffusion coefficient and dye-loading are attributed to the specific morphology of the ZnO-NS. A further improvement in the efficiency of the DSSC with ZnO-NS could be achieved through the electrophoretic deposition (EPD) of a very thin layer (3 μm) of titanium dioxide nanoparticles (TiO 2-NPs of average size 14 nm) onto the ZnO-NS layer (12 μm). Notwithstanding a decrease in the effective electron diffusion coefficient (3.07 × 10 -3 cm 2 s -1) in the TiO 2-NP/ZnO-NS film, with reference to that in the ZnO-NS film (3.59 × 10 -3 cm 2 s -1), a far higher cell efficiency was obtained in favor of the cell with TiO 2-NP/ZnO-NS (7.07%), compared to that of the cell with bare ZnO-NS (6.06%); this enhancement in the η of the cell with TiO 2-NP/ZnO-NS is ascribed to an increased dye-loading in favor of its cell (3.92 × 10 -7 mol cm -2), with reference to that in the case of the cell with bare ZnO-NS (2.66 × 10 -7 mol cm -2). As against the common ruthenium dyes, such as N3 and N-719, a metal-free dye, coded as D149, was used in this research. The efficiency achieved for the best DSSC in this work is the highest ever reported for a DSSC with ZnO as the main semiconductor material.

頁(從 - 到)3448-3455
期刊Energy and Environmental Science
出版狀態Published - 2011 9月

All Science Journal Classification (ASJC) codes

  • 污染
  • 核能與工程
  • 可再生能源、永續發展與環境
  • 環境化學


深入研究「Highly efficient dye-sensitized solar cell with a ZnO nanosheet-based photoanode」主題。共同形成了獨特的指紋。