Impact angle of maximum erosion rate of wear resistant spheroidal graphite cast iron eroded by SiO2 and Al2O3 particles

F. Y. Hung, L. H. Chen, T. S. Lui

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

The influence of matrix structure, erodent and impact angle on the wear resistance of pearlitic and bainitic spheroidal graphite cast irons was studied using impact tests with SiO2 and Al2O3 particles. Erosion with Al2O3 particles produced significantly larger materials removal rates for both irons. The bainitic ADI was more wear resistant than the pearlitic PDI specimens at impact angles > 30°. The type of erodent did not affect the impact angle of maximum erosion rate for ADI, but for the PDI specimens this angle was higher with Al 2O3 particles than with SiO2. Examination of the wear surface by SEM provided evidence of many brittle cracks on PDI specimens following impact with Al2O3; this correlates with the higher impact angle of maximum wear for this material-erodent combination. The higher fracture toughness of the Al2O3 particles also played a role in the erosion wear behaviour observed for both PDI and ADI.

原文English
頁(從 - 到)505-513
頁數9
期刊International Journal of Cast Metals Research
16
發行號5
DOIs
出版狀態Published - 2003 一月 1

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys

指紋 深入研究「Impact angle of maximum erosion rate of wear resistant spheroidal graphite cast iron eroded by SiO<sub>2</sub> and Al<sub>2</sub>O<sub>3</sub> particles」主題。共同形成了獨特的指紋。

引用此