Impact of Entanglement Density on Solution Electrospinning: A Phenomenological Model for Fiber Diameter

Chi Wang, Yu Wang, Takeji Hashimoto

研究成果: Article同行評審

43 引文 斯高帕斯(Scopus)

摘要

The rheological properties of poly(N-isopropylacrylamide, PNIPAM) in dimethylformamide solvent were investigated and correlated with solution electrospinnability. The jet diameter was measured by using the light scattering technique during the electrospinning in the straight jet region prior to the jet whipping. The diameter of the straight jet end is independent of the solution concentration (or viscosity within the range of 15-2000 mPa·s). Thus, the final fiber diameter df observed on the grounded collector is dominantly controlled by the jet-whipping process. According to the present PNIPAM solution and other different polymer solutions, df is correlated with the solution concentration ø. A master curve is constructed by using the following equation: df/df,e = (ø/øe)2.5, where df,e is the diameter of the fibers electrospun from the solutions with an entanglement concentration of øe, above which the specific viscosity starts to increase with ø according to ø3.7 or ø4.7, depending upon the given polymer/solvent pair. The derived exponent of 2.5 is in good agreement with the theoretical exponent value of 2.3 provided that df is proportional to the entanglement density ν(ø) ∼ ø2.3 (entangled strands per unit volume of the solution). Our results imply that the plateau modulus (elasticity) of the entangled polymer solution rather than its viscosity plays a major role in determining the final fiber diameter. The entangled polymer solutions behave like elastic swollen gels during electrospinning because of the high deformation rates. We propose that the deformation-induced structure formation in the jet eventually results in the fiber with the concentration-dependent diameter.

原文English
頁(從 - 到)7985-7996
頁數12
期刊Macromolecules
49
發行號20
DOIs
出版狀態Published - 2016 10月 25

All Science Journal Classification (ASJC) codes

  • 有機化學
  • 聚合物和塑料
  • 無機化學
  • 材料化學

指紋

深入研究「Impact of Entanglement Density on Solution Electrospinning: A Phenomenological Model for Fiber Diameter」主題。共同形成了獨特的指紋。

引用此